铝合金耐磨性差、特殊条件下耐蚀性差的缺点限制了它的进一步利用,对铝合金进行表面处理长期以来一直是扩大铝合金使用范围地行之有效的方法.文章综述了铝合金的各种表面处理方法,比较了它们的优缺点,指出表面氧化是铝合金表面处理的主流,复合处理、纳米化处理将是今后铝合金表面处理的主要研究方向.
Abstract：The applications of aluminum alloy have been limited by its poor wear resistance and corrosion resistance under special conditions.Surface treatment technology has been a method for a long time as an effective solution to extend the application area.Various surface treatment methods of aluminum alloy have been reviewed,and their advantages and disadvantages have been discussed in detail.The surface oxidation has been indicated as the current mainstream of the surface treatment of aluminum alloys,and complex treatment as well as nanotechnology will be the main research directions of the future surface treatment of aluminum alloys.
[1]GUZMAN L,BONINI G,ADAMI M,et al.Mechanicalbehaviour of nitrogen implanted aluminum alloys[J].SurfCoat Technol,1996,83:284.
[2]WATKIMS K G,LIU Z,MEMAHON M,et al.Influenceof the over lapped area on the corrosion behaviour of lasertreated aluminum alloy[J].Materials Science and Engineer-ing,1998,A252:292-300.
[3]吴敏,孙勇.铝及其合金表面处理的研究现状[J].表面技术,2003,32(3):13-15.
[4]THOMO S G E.Porous anodic alumina:fabrication,char-acterization and app lications[J].Thin Solid Films,1997,297:192.
[5]PATERMARAKIS G,PAPANDREADIS N.Effect of thestructure of porous anodic Al2O3films on themechanism oftheir hydration and pore closure during hydrothermal treat-ment[J].Electrochemica Acta,1993,38(10):1413.
[6]ZHOU W Q,SHAN D,HAN E H,et al.Structure andformation mechanism of phosphate conversion coating ondiecast AZ91D magnesium alloy[J].Corrosion Science,2008,50(2):329-337.
[7]石磊,石勇,董新民.铝及铝合金电镀[J].表面技术,2007,36(4):87-88.
[8]杨蔺孝,杨岑.铝材耐磨耐烧蚀特种氧化成膜机理的研究与应用[J].电镀与环保,1992,12(2):131.
[9]李素琴,段绍范,段晓楠,等.铝合金脉冲硬质阳极氧化工艺与膜层性能的研究[J].材料保护,1994,27(3):61.
[10]顾德恩,陈金菊,冯哲圣,等.铝箔表面复合阳极氧化膜研究[J].功能材料,2004,5(35):600-602.
[11]刘世永,张会臣,高学敏,等.6063铝合金复合硬质阳极氧化及摩擦行为研究[J].轻合金加工技术,2004,32(4):42-44.
[12]赵斌,董世知.铝合金化学镀Ni-P合金的研究进展[J].电镀与涂饰,2008,27(1):24-26.
[13]王艳芝.铝合金化学镀Ni2Fe2P2B,工艺研究[J].电镀与环保,2002,22(4):20-22.
[14]郭瑞光,杨杰,康娟.铝合金表面钛酸盐化学转化膜研究[J].电镀与涂饰,2006,25(1):46-48.
[15]HINTON B R,AMOTT O R,RYAN N E.Cerinm conver-sion coatings for the corrosion protection of aluminum[J].Mater Forum,1986,9(3):162-165.
[16]MANSFELD F,KIM L,SHIN H.Surface modificat ion-of A l alloys and Al based metal matrix composites bychemical passivation[J].Corros Sci,1987,27(9):997.
[17]吴桂香,陈东初,李文芳,等.铝型材表面环保型稀土转化膜制备与工艺优化[J].轻合金加工技术,2006,34(10):40-43.
[18]COHEN S M.Review:Replacements for chromiump re-treatment on aluminum[J].Corrsoion,1995,51(1):711.
[19]吕勇武,熊金平.铝合金表面无铬化学转化膜工艺研究[J].电镀与涂饰,2007,26(12):25-28.
[20]陈东初,黄柱周,李文芳.铝合金表面无铬化学转化膜的研究[J].表面技术,2005,34(6):38-39.
[21]孙国平,杨向明.改善铸铝基体性能的热喷涂技术[J].铁道机车车辆工人,1997(5):28-29.
[22]李言祥,马剑.铝基体表面等离子喷涂后激光二次熔覆陶瓷层的研究[J].应用激光,1998,18(6):245-2481.
[23]徐荣正,宋刚,刘黎明.铝合金表面电弧喷涂铝涂层工艺与性能[J].焊接学报,2008,29(6):109-113.
[24]战再吉,马欣新,冯莉丽,等.铝合金等离子体淹没氮离子注入层的摩擦学性能研究[J].摩擦学报,1998,18(4):3002304.
[25]廖家轩,夏立芳.铝合金等离子体基离子注入氮/钛层的结构[J].中国有色金属学报,2001,11(3):450-453.
[26]汤宝寅,张更伟,王小峰,等.氮、氧及金属离子注入铝合金表面改性层摩擦磨损性能研究[J].摩擦学报,2003,123(4):287-290.
[27]王齐伟,左秀荣.直流磁控溅射在铝衬底上沉积(TixAly)N薄膜及其性能研究[J].真空科学与技术学报,2008,28(4):351-354.
[28]李华平,柴广跃,彭文达,等.Al薄膜覆Al基板的物理特性[J].电子元件与材料,2007,10:54-56.
[29]徐重,张高会,张平则,等.双辉等离子表面冶金技术的新进展[J].中国工程科学,2005,7(6):73-78.
[30]赵新,金杰,姚健铨.激光表面改性技术的研究与发展[J].光电子.激光,2000,11(3):324-328.
[31]纪红,许越.铝合金激光表面强化的研究进展[J].材料科学与工艺,2003,11(2):220-224.
[32]蔡,杨晓豫.ZL109激光表面改性处理——激光表面重熔[J].上海交通大学学报,1999,33(7):804-812.
[33]陈华,孟繁晶.铝合金激光熔覆[J].吉林工学院学报,1998,19(4):312-314.
[34]卢长亮,胡芳友.变形铝合金激光熔覆工艺研究[J].中国表面工程,2007,20(6):44-47.
[35]蔡,杨晓豫,卜晓梅,等.ZL109激光表面改性处理-激光表面合金化[J].上海交通大学学报,1999,33(7):36-40.
基本信息:
DOI：
中图分类号:TG178
引用信息:
[1]张高会,黄国青,徐鹏等.铝及铝合金表面处理研究进展[J].中国计量学院学报,2010,21(02):174-178.
基金信息:
浙江省科技厅资助项目(No.2007C21139);; 国家青年基金资助项目(No.10802083)